Loss circulation material composition having alkaline nanoparticle based dispersion and water soluble hydrolysable ester

ABSTRACT

A lost circulation material (LCM) is provided having an alkaline nanosilica dispersion and an ester activator. The alkaline nanosilica dispersion and the ester activator may form a gelled solid after interaction over a contact period. Methods of lost circulation control using the LCM are also provided.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional of and claims priority from U.S. Non-provisional application Ser. No. 15/679,890 filed Aug. 17, 2017, and titled “LOSS CIRCULATION MATERIAL COMPOSITION HAVING ALKALINE NANOPARTICLE BASED DISPERSION AND WATER SOLUBLE HYDROLYSABLE ESTER,” a copy of which is incorporated by reference in its entirety for purposes of United States patent practice.

BACKGROUND Field of the Disclosure

The present disclosure generally relates to controlling lost circulation in a well during drilling with a drilling fluid. More specifically, embodiments of the disclosure relate to lost circulation materials (LCMs).

Description of the Related Art

Various challenges are encountered during drilling and production operations of oil and gas wells. For example, fluids used in drilling, completion, or servicing of a wellbore can be lost to the subterranean formation while circulating the fluids in the wellbore. In particular, the fluids may enter the subterranean formation via depleted zones, zones of relatively low pressure, lost circulation zones having naturally occurring fractures, weak zones having fracture gradients exceeded by the hydrostatic pressure of the drilling fluid, and so forth. The extent of fluid losses to the formation may range from minor losses (for example less than 10 barrels/hour ((bbl/hr), also referred to as seepage loss, to severe (for example, greater than 100 bbl/hr), or higher, also referred to referred to as complete fluid loss. As a result, the service provided by such fluid is more difficult or costly to achieve.

Such lost circulation can be encountered during any stage of operations and occurs when drilling fluid (or drilling mud) pumped into a well returns partially or does not return to the surface. While de minimis fluid loss is expected, excessive fluid loss is not desirable from a safety, an economical, or an environmental point of view. Lost circulation is associated with problems with well control, borehole instability, pipe sticking, unsuccessful production tests, poor hydrocarbon production after well completion, and formation damage due to plugging of pores and pore throats by mud particles. Lost circulation problems may also contribute to non-productive time (NPT) for a drilling operation. In extreme cases, lost circulation problems may force abandonment of a well

SUMMARY

Lost circulation materials (LCMs) are used to mitigate lost circulation by blocking the path of the drilling mud into the formation. The type of LCM used in a lost circulation situation depends on the extent of lost circulation and the type of formation. Existing LCMs may perform poorly in mitigation and prevention of moderate lost circulation and seepage type lost circulation, and may not be suitable for controlling severe loss of circulation. Costs incurred in loss circulation situations may be due to losses of drilling fluids, losses of production, and the costs of LCMs.

In one embodiment, a method to control lost circulation in a lost circulation zone in a wellbore is provided. The method includes introducing a lost circulation material (LCM) into the wellbore such that the LCM contacts the lost circulation zone and reduces a rate of lost circulation into the lost circulation zone as compared to a period before introducing the LCM. The LCM includes an alkaline nanosilica dispersion and a water soluble ester. In some embodiments, the LCM consists of the alkaline nanosilica dispersion and the water soluble ester. In some embodiments, the water soluble ester includes at least one of a glycol ester, a polyethylene glycol ester, an alkyl ester, and an ester of a carboxylic acid and an alcohol. In some embodiments, the water soluble ester includes at least one of ethyl acetate, ethyl formate, ethylene glycol diacetate, diethylene glycol dilactate, and ethylene glycol diformate. In some embodiments, the method includes maintaining the alkaline nanosilica dispersion and the water soluble ester in contact with the lost circulation zone for a contact period, such that the alkaline nanosilica dispersion forms a gelled solid. In some embodiments, the contact period is in a range of 0.5 hours to 24 hours. In some embodiments, the water soluble ester is an amount in the range of 0.1 percent by volume of the total volume (v/v %) to 10 v/v %. In some embodiments, the lost circulation zone has a temperature that is at least 100° F. In some embodiments, the method includes mixing the alkaline nanosilica dispersion and the water soluble ester to form the LCM at the surface before introducing the LCM into the wellbore. In some embodiments, the LCM includes at least one of calcium carbonate particles, fibers, mica, and graphite. In some embodiments, the fibers include at least one of ester fibers, polypropylene fibers, starch fibers, polyketone fibers, ceramic fibers, glass fibers and nylon fibers. In some embodiments, the pH of the alkaline nanosilica dispersion is at least 8.

In another embodiment, a lost circulation material (LCM) composition is provided that includes an alkaline nanosilica dispersion and a water soluble ester, such that the water soluble ester selected to form a gelled solid with the alkaline nanosilica dispersion after a period at an elevated temperature. In some embodiments, the period is in a range of 0.5 hours to 24 hours. In some embodiments, the water soluble ester is an amount in the range of 0.1 percent by volume of the total volume (v/v %) to 10 v/v %. In some embodiments, the water soluble ester includes at least one of ethyl acetate, ethyl formate, ethylene glycol diacetate, diethylene glycol dilactate, and ethylene glycol diformate.

In another embodiment, a solid gelled material useful for mitigating lost circulation is provided. The solid gel material forms by introducing an alkaline nanosilica dispersion and a water soluble ester to a lost circulation zone. The nanosilica dispersion includes amorphous silicon dioxide and water, such that the nanosilica dispersion and the water soluble ester contact the lost circulation zone for a period such that the solid gelled material forms. In some embodiments, the ester includes at least one of ethyl acetate, ethyl formate, ethylene glycol diacetate, diethylene glycol dilactate, and ethylene glycol diformate. In some embodiments, the water soluble ester includes an amount in the range of 0.1 percent by volume of the total volume (v/v %) to 10 v/v %.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a photograph of the solid formed by a mixture of an alkaline nanosilica dispersion with an ethyl lactate activator; and

FIG. 2 is a photograph of the solid formed by a mixture of an alkaline nanosilica dispersion with an ethyl lactate activator.

DETAILED DESCRIPTION

The present disclosure will be described more fully with reference to the accompanying drawings, which illustrate embodiments of the disclosure. This disclosure may, however, be embodied in many different forms and should not be construed as limited to the illustrated embodiments. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the disclosure to those skilled in the art.

Embodiments of the disclosure include a lost circulation material (LCM) that includes an alkaline nanosilica dispersion and a water soluble hydrolysable ester activator. The LCM may mitigate or prevent lost circulation in a well, as well as provide seepage control and minimize or prevent fluid loss. In some embodiments, the ester activator may include ethyl lactate. In some embodiments, the ester activator may include ethyl acetate, ethyl formate, ethylene glycol diacetate, diethylene glycol dilactate, and ethylene glycol diformate. The alkaline nanosilica dispersion may have a pH of at least 8, such as in the range of about 8.5 to about 10.5, before interaction with the activator. The alkaline nanosilica dispersion and ester activator LCM may be introduced into a lost circulation zone in a wellbore, such that the alkaline nanosilica dispersion and ester activator LCM alters the lost circulation zone. The alkaline nanosilica dispersion and ester activator LCM may be allowed to interact with the lost circulation zone for a period to enable the in-situ formation of a gelled solid as a result of the interaction between the alkaline nanosilica dispersion and an acid generated from the ester activator via hydrolysis.

Alkaline Nanosilica Dispersion and Ester Activator LCM

In some embodiments, an LCM includes an alkaline nanosilica dispersion and a water soluble hydrolysable ester activator. The alkaline nanosilica dispersion may include amorphous silicon dioxide and an aqueous medium. For example, in some embodiments, the alkaline nanosilica dispersion may be formed using water or other suitable aqueous mediums (for example, water and glycerin). In some embodiments, the nanosilica dispersion has a pH of about 8.5 to about 10.5 at 25° C. before interaction with the activator. In some embodiments, the nanosilica dispersion has a pH of at least 8 before interaction with the activator. In some embodiments, the nanosilica dispersion has a specific gravity of 1.2 (g/ml). In some embodiments, the nanosilica dispersion may be obtained from Evonik Corporation of Parsippany, N.J., USA.

In some embodiments, the ester may include a glycol ester, a polyethylene glycol ester, an alkyl ester, and an ester of a carboxylic acid and an alcohol. In some embodiments, the water insoluble hydrolysable ester activator may include ethyl lactate. In other embodiments, the ester activator may include other water soluble hydrolysable esters, such as ethyl acetate, ethyl formate, ethylene glycol diacetate, diethylene glycol dilactate, and ethylene glycol diformate. In some embodiments, the weight ratio of the alkaline nanosilica dispersion to the ester activator is in the range of 50:1 to 80:1. For example, in some embodiments, the weight ratio of the alkaline nanosilica dispersion to the ester activator is 66:1. In some embodiments, the ester activator may be in an amount in the range of about 0.1 percent by volume of the total volume (v/v %) to about 10 v/v %

In some embodiments, the nanosilica dispersion and ester activator LCM may include additional materials. For example, in some embodiment the nanosilica dispersion and ester activator LCM may include calcium carbonate particles, fibers (for example, ester fibers, polypropylene fibers, starch fibers, polyketone fibers, ceramic fibers, glass fibers nylon fibers, or combinations thereof), mica, graphite, or combinations thereof.

The alkaline nanosilica dispersion and ester activator LCM may be introduced (for example, by pumping) into a lost circulation zone in a wellbore to control lost circulation. In some embodiments, the alkaline nanosilica dispersion and ester activator LCM may be allowed to interact with the lost circulation zone for a contact period. The contact period may be of sufficient duration to enable formation of a solid as a result of the interaction between the alkaline nanosilica dispersion and the ester activator. The formed solid may alter the lost circulation zone (for example, by entering and blocking porous and permeable paths, cracks, and fractures in a formation in the lost circulation zone, such as forming a structure in a mouth or within a fracture). In some embodiments, the ester and the alkaline nanosilica dispersion may be introduced simultaneously to the lost circulation zone. In other embodiments, the ester activator may be introduced separately from the alkaline nanosilica dispersion to the lost circulation zone.

In some embodiments, the contact period may be in the range of about 0.5 hours to about 24 hours. For example, in some embodiments the contact period may be about 16 hours. In some embodiments, the contact period may be selected based on the formation type of the lost circulation zone.

As shown infra, the alkaline nanosilica dispersion and ester activator may form a solid LCM after a sufficient period. In some embodiments, the gelling of the alkaline nanosilica dispersion may be controlled by varying the concentration of the ester activator, and the gelling may be controlled by changing the pH of the LCM. For example, increasing concentrations of the ester activator may increase the pH of the LCM and increase the rate of gelation of the LCM. Additionally, the ester activator exhibits no precipitation with the alkaline nanosilica dispersion at elevated temperature, thus enabling use of the LCM composition as a single fluid pill (that is, without staged mixing of each component). Consequently, the delayed and controlled gelling of the alkaline nanosilica dispersion LCM may provide for easier pumping of the LCM. The alkaline nanosilica dispersion and ester activator LCM may be used at elevated temperatures in a wellbore such as, for example, temperatures greater than 100° F., such as 300° F. In some embodiments, the alkaline nanosilica dispersion and ester activator LCM may be used in lost circulation zones having temperatures below 100° F. In such embodiments, the LCM may include a catalyst to increase the rate of hydrolysis of the ester. In some embodiments, the catalyst may include hydrochloric acid, sulfuric acid, or other suitable acids. Moreover, the environmentally friendly properties of the alkaline nanosilica dispersion and ester activator LCM may minimize or prevent any environmental impact and effect on ecosystems, habitats, population, crops, and plants at or surrounding the drilling site where the alkaline nanosilica dispersion and ester activator LCM is used.

EXAMPLES

The following examples are included to demonstrate embodiments of the disclosure. It should be appreciated by those of skill in the art that the techniques and compositions disclosed in the example which follows represents techniques and compositions discovered to function well in the practice of the disclosure, and thus can be considered to constitute modes for its practice. However, those of skill in the art should, in light of the present disclosure, appreciate that many changes can be made in the specific embodiments which are disclosed and still obtain a like or a similar result without departing from the spirit and scope of the disclosure.

The following non-limiting example of an alkaline nanosilica dispersion was tested with a water soluble hydrolysable ester activator.

The alkaline nanosilica dispersion used was IDISIL® SI 4545 manufactured by Evonik Corporation of Parsippany, N.J., USA. The properties of the nanosilica dispersion are described in Table 1

TABLE 1 Properties of Nanosilica Dispersion Nanosilica dispersion pH @ 25° C. 8.5-10.5 Specific Gravity 1.2 (grams/milliliter (g/ml)) Viscosity @ 25° C. (cP) <30 Visual Appearance White/Off White Weight % SiO2 45

A composition was prepared using the alkaline nanosilica dispersion and ethyl lactate. 100 milliliters (ml) of the alkaline nanosilica dispersion was added to an empty beaker. 2 grams (g) of ethyl lactate (that is, 1 gram of ethyl lactate per 66 grams of alkaline nanosilica dispersion) was added to the alkaline nanosilica dispersion and mixed using a stirrer. The alkaline nanosilica dispersion-ethyl lactate mixture was subjected to static aging in an aging cell. The cell was static aged at a temperature of about 250° F. for about 16 hours to simulate downhole conditions.

After 16 hours of static aging, the alkaline nanosilica dispersion was converted into a solid. The ethyl lactate hydrolyzed in the aqueous medium (for example, water) of the alkaline nanosilica dispersion to generate a resulting acid. The acid acted as an activator that destabilized the alkaline nanosilica dispersion and produced a solid. FIGS. 1 and 2 are photographs 100 and 200 respectively of the solid formed by the mixture of the alkaline nanosilica dispersion with the ethyl lactate activator. The formation of the solid after static aging at the elevated temperature of 250° F. shows that the alkaline nanosilica dispersion can behave as an LCM when introduced with a water soluble hydrolysable ester activator.

Ranges may be expressed in the disclosure as from about one particular value, to about another particular value, or both. When such a range is expressed, it is to be understood that another embodiment is from the one particular value, to the other particular value, or both, along with all combinations within said range.

Further modifications and alternative embodiments of various aspects of the disclosure will be apparent to those skilled in the art in view of this description. Accordingly, this description is to be construed as illustrative only and is for the purpose of teaching those skilled in the art the general manner of carrying out the embodiments described in the disclosure. It is to be understood that the forms shown and described in the disclosure are to be taken as examples of embodiments. Elements and materials may be substituted for those illustrated and described in the disclosure, parts and processes may be reversed or omitted, and certain features may be utilized independently, all as would be apparent to one skilled in the art after having the benefit of this description. Changes may be made in the elements described in the disclosure without departing from the spirit and scope of the disclosure as described in the following claims. Headings used described in the disclosure are for organizational purposes only and are not meant to be used to limit the scope of the description. 

What is claimed is:
 1. A lost circulation material (LCM) composition, comprising: an alkaline nanosilica dispersion, wherein the alkaline nanosilica dispersion has a pH in the range of 8.5 to 10.5; and a water soluble ester, the water soluble ester selected to form a gelled solid with the alkaline nanosilica dispersion after a period comprising a range of 0.5 hours to 24 hours, wherein the water soluble ester comprises ethyl lactate and the weight ratio of the alkaline nanosilica dispersion to the water soluble ester is in the range of 50:1 to 80:1; and a catalyst selected to increase a hydrolysis rate of the water soluble ester.
 2. A solid gelled material useful for mitigating lost circulation, where the solid gelled material forms by introducing an alkaline nanosilica dispersion, a water soluble ester, and a catalyst selected to increase a hydrolysis rate of the water soluble ester to a lost circulation zone, the nanosilica dispersion comprising amorphous silicon dioxide and water, such that the nanosilica dispersion and the water soluble ester contact the lost circulation zone for a period comprising a range of 0.5 hours to 24 hours such that the solid gelled material forms, wherein the alkaline nanosilica dispersion has a pH in the range of 8.5 to 10.5, and wherein the water soluble ester comprises ethyl lactate and the weight ratio of the alkaline nanosilica dispersion to the water soluble ester is in the range of 50:1 to 80:1.
 3. The solid gelled material of claim 2, wherein the water soluble ester is introduced separately from the alkaline nanosilica dispersion to the lost circulation zone.
 4. The solid gelled material of claim 2, wherein the water soluble ester and the alkaline nanosilica dispersion are introduced simultaneously to the lost circulation zone.
 5. The LCM of claim 1, wherein the catalyst comprises hydrochloric acid.
 6. The solid gelled material of claim 2, wherein the catalyst comprises hydrochloric acid. 